金属学报(英文版)
Au investigation was carried ont of the effect of Y addition upon the internal stress of Al_2O_3 scale formed during oxidation of sputtering coating on Co-30Cr-6Al alloy and the growth stress of oxidized film on Fe-23Cr-5Al alloy heating up to 900℃ in air,using a specially designed deflection method from thin strip specimen with coat- ings,ion-implanted Y on one side and oxidized onto both sides.Results indicate that Y may decrease the internal stress of oxide scale on 2×10~(17) Y~+/cm~2 implanted Co- 30Cr-6Al coating,and increase one on 2×10~(16) Y~+/cm~2 implanted Fe-23Cr-5Al alloy. This seems due to whether or not Y promotes the plastic deformation of oxide scale.In addition,at initial oxidation stage,the change of growth stress of oxide scale formed on Y-implanted Co-30Cr-6Al coating may be related to the influence of Y on oxidation process of the coating.